The HF SG460 Ultra Late Drying (F) NS series is used for glass and various hardened materials. Specially designed for UV adhesive resistance, inks has excellent weather resistance, drug resistance, and moisture resistance compared to ordinary glass inks. It is a series specially developed to meet the Chinese VOCs<GB 38507-2020>standard.
urethane resin
3-component isocyanate hardening type
Suitable for glass and various hardened materials.
Excellent glossiness.
Excellent weather resistance, acid resistance, alkali resistance, solvent resistance, water resistance, friction resistance, etc.
T-39 T-41
It is recommended to use polyester or nylon screen printing with a mesh size of 200-460 for screen printing
Room temperature 80 ℃ x 50-60 minutes: Various materials that have undergone hardening treatment
Baking at 150 ℃ x 30-50 minutes: glass
Project | Method | Evaluate | Result |
Adhesiveness | Cross cut at 1mm intervals and use tape for peeling test | No peel off | Qualified |
Hardness | According to the pencil hardness tester, 45 ° × 750g | No obvious traces | 2H qualified |
Cold and hot cycle resistance test | -20 ℃ × 30 minutes → 80 ℃ × 30 points are divided into one cycle, and this condition is repeated 10 times. After the end of the cycle, cross cut at 1mm intervals and use tape for peeling test | No change in appearance, no detachment | Qualified |
Alcohol resistance | Wrap 500g of the French code with gauze, which contains grade 1 methanol and rub back and forth 50 times | Colorless transfer on gauze, no peeling after back and forth wiping | Qualified |
rub resistance | Wrap 500g of French code with gauze and wipe back and forth 50 times | Wipe back and forth without any detachment | Qualified |
Boiling resistance | After immersing in boiling water for 3 hours, let it stand at room temperature for more than 2 hours, cross cut at 1mm intervals, and then use tape for peeling test | No change in appearance, no detachment | Qualified |